Fiberon™ PA6-CF20 is a carbon fibre reinforced PA6 (Nylon 6) filament. The carbon fibre reinforcement provides significantly improved stiffness, strength and heat resistance with outstanding layer adhesion.
0.5kg - Black
In stock
Fiberon™ PA6-CF20
Exceptional stiffness, strength, heat resistance up to 215°C, with superior layer adhesion!
The PA6-CF20 filament from the Fiberon line of high-performance polymers is a PA6-based material reinforced with 20% carbon fiber, offering exceptional strength, stiffness, and isotropic rigidity. With a heat resistance reaching up to 215 ºC, PA6-CF20 is suitable for demanding applications that require stability under high temperatures. It also features Fiber Adhesion™ Technology, which promotes superior layer adhesion, resulting in robust, cohesive printed parts. These properties make PA6-CF20 ideal for challenging uses in automotive, composite manufacturing, and industrial components, where performance and durability are critical. If a filament with even better mehanical properties and reduced moisture sensitivity is required, please see the Fiberon PA612-CF15 filament.
Printing Requirements
- All-metal hotend 280˚C+
- Hardened nozzle
- Filament dryer
- Annealing post printing
- Moisture conditioning after Annealing
Specification
TDS Download SDS Download
General information | |
| Material | PA |
| Format | 500 g / 3 kg |
| Density | (ISO 1183) 1.17 g/cm³ |
| Filament diameter | 1.75 mm |
| Filament length | (Ø 1.75 mm-0.5 Kg) ±177.7 m / (Ø 1.75 mm-3 Kg) ±1066.0 m |
Electrical properties | |
| Surface electrical resistivity | (ANSI ESD S11.11) OL, >10¹² Ohm |
Printing properties | |
| Printing temperature | 280 – 300 ºC |
| Print bed temperature | 40 – 50 ºC |
| Chamber temperature | 20 – 25 ºC |
| Cooling fan | ✗ |
| Recommended printing speed | Max. 300 mm/s |
| Recommended nozzle | Hardened Steel |
Mechanical properties | |
| Charpy impact strength | (ISO 179) 11.0 ± 0.3 KJ/m² |
| Elongation at break | (ISO 527) XY: 2.1 ± 0.2 % / Z: 1.9 ± 0.4 % |
| Tensile strength | (ISO 527) XY: 109.3 ± 2.4 MPa / Z: 54.0 ± 5.2 MPa |
| Tensile modulus | (ISO 527) XY: 8636.5 ± 211.4 MPa / Z: 3759.5 ± 118.5 MPa |
| Flexural strength | (ISO 306) XY: 161.0 ± 3.9 MPa / Z: – MPa |
| Flexural modulus | (ISO 178) XY: 7037.6 ± 205.4 MPa / Z: – MPa |
| Surface hardness | – |
Thermal properties | |
| Melting temperature | (DSC) 218.5 ºC |
| Softening temperature | – ºC |
| Heat deflexion temperature | (ISO 75) @ 0.45 MPa: 215 ºC / @ 1.8 MPa: 173 ºC |
Specific properties | |
| Transparency | ✗ |
| Flammability classification | UL 94 HB @ 1.5 mm |
| Chemical resistance | ✓ |
| Weight | 0.5 kg |
|---|---|
| Dimensions | 210 × 210 × 50 cm |
| Brand | |
| Colour | Black |
Related products
Add to cart DetailsBuy NowNylon-Carbon Fibre composite Natural (Black) 1.75mm Filament – comes on a vacuum packed 1kg cardboard reel and is a tough and semi-flexible material that offers high impact and abrasion resistance. It is an ideal choice for printing durable parts.
- Add to cart DetailsBuy Now
ePAHT-CF is a PA6-based material developed by eSUN and LUVOCOM, to which 15% high-rigidity carbon fibre has been added. The filament has high strength, mechanical and thermal properties higher than other nylon filaments.
Add to cart DetailsBuy Now1kg high quality premium and well priced 1.75mm PLA Pro 3D Printer composite CF filament. It was engineered, similar to other PLA+ materials, for better printing performance. 15% CF
Reviews
There are no reviews yet.